1 D) exhibited a decreasing trend with rising temperature; within the Si doping range of 0 mol.% to 4 mol.%, the HA mass ratio ranged from 60 wt% to 40 wt%, diminishing with higher silicon content.
← all excerpts
Optimizing silicon doping levels for enhanced osteogenic and angiogenic properties of 3D-printed biphasic calcium phosphate scaffolds: An <i>in vitro</i> screening and <i>in vivo</i> validation study.