Meanwhile, the hydrogen evolution results in Figure 4 b indicate that, during the whole immersion time, the corrosion rate of the blank concentration increased continuously, while the corrosion rate showed a decreasing trend with the addition of a corrosion inhibitor.
← all excerpts
Effect of the Sodium Silicate Inhibitor on the Corrosion Protection of AZ31 Magnesium Alloy.