Sulfobetaine-Modified Poly(butylene succinate) with Fine-Tuned Mechanical and Lubricating Properties in Melted Film Discs.

ACS Appl Mater Interfaces · 2026 · PMC12884459 · PMID 41560498

Europe PMC DOI

hedged sentence

—

closest p

—

boldest claim

The sentences

a decreasing trendno p-value reported

A decreasing trend in compressive strength was observed across the series of double bond-incorporated copolymers: P(BS 90 -co - c BS 10 ), P(BS 85 - co - c BS 15 ), P(BS 80 - co - c BS 20 ), P(BS 75 - co - c BS 25 ), P(BS 65 - co - c BS 35 ), and P(BS 50 - co - c BS 50 ), with values of 46 MPa ± 4.2, 44 MPa ± 2.5, 40 MPa ± 2.1, 29 MPa ± 3.9, 22MPa ± 1.2, and 15 MPa ± 2.0, respectively.