Single-Crystal MoO₃ Micrometer and Millimeter Belts Prepared from Discarded Molybdenum Disilicide Heating Elements.

Figure 8a shows the TG-DTA curves of powdery α-MoO 3 microbelts, initial weight was around 3.293 mg, and its weight had hardly significant change before 700 °C as well as the TG curve without ant stage decomposition, and only a loss of weight was about 4.03% due to the evaporation of water molecules in the product, so that powdery α-MoO 3 microbelts had good thermal stability before 700 °C.