Thermal Stability and Rheological Properties of Epoxidized Natural Rubber-Based Magnetorheological Elastomer.

As referred to in Figure 5 a and Figure 5 b, a decreasing trend was observed for all CIP loadings and applied magnetic fields in such a way that the storage modulus steadily decreased as the strain amplitude increased from approximately 0.01% to 1%, and it remarkably diminished beyond these values up to 10%.

also in 47,180 other papers

The results indicated that the polymer decomposition of the ENR-based MRE with the increase of CIPs started to occur at a high temperature since T onset exhibited an increasing trend.

also in 63,971 other papers