Compositional Effects on Indentation Mechanical Properties of Chemically Strengthened TiO₂-Doped Soda Lime Silicate Glasses.

However, it is possible to draw some general observations based on the results: (1) increasing the SiO 2 content tends to increase the Δ H CS ; (2) increasing the TiO 2 content tends to slightly decrease Δ H CS ; and (3) increasing the CaO content tends to give an increasing trend of Δ H CS with a maximum around 9 mol%.

also in 63,971 other papers

The Δ H CS generally has a decreasing trend with increasing TiO 2 content (see Figure S3 in the Supplementary Materials ).

also in 47,180 other papers