Rapid Microstructure Homogenization of a Laser Melting Deposition Additive Manufactured Ti-6.5Al-3.5Mo-1.5Zr-0.3Si Alloy by Electropulsing.

It could be seen from Figure 6 that the β t content presents an increasing trend as EPT voltage increases.

also in 63,971 other papers

While the yield strengths of the EPT8 and EPT9 samples are 726 MPa and 771 MPa, exhibiting a decreasing trend generally, which could be attributed to the decrease of α p and the increase of β t [ 11 ], the EPT8 sample possesses the lowest yield strength, which is corresponding to the highest area fraction value of β t .

also in 47,180 other papers