Evolution of Microstructural and Mechanical Properties of Alloy 617B During Service on a Key-Component Test Platform at 700 °C.

After 10,000 h of service, the fracture showed a trend of intergranular fracture ( Figure 2 b), with small dimples and numerous secondary cracks visible on the grain surface at high magnification ( Figure 2 e).