As can be seen from Figure 8 , with the increase in tempering temperature, the M 3 C, M 2 (C, N), M (C, N), M 23 C 6 carbide peak content is unchanged, and the M 7 C 3 peak appeared to show a clear trend of first declining and then rising.
← all excerpts
Design and Optimization of W-Mo-V High-Speed Steel Roll Material and Its Heat-Treatment-Process Parameters Based on Numerical Simulation.