In the analysis of crack behavior at a 0° orientation, it is observed that as the stretching rate increases from a baseline of 2 mm/min, the crack tip strain growth exhibits a negative trend.
← all excerpts
Fatigue failure of prefabricated crack HTPB(hydroxyl-terminated polybutadiene) propellant under strain control.