At the same time, it can also be seen from the figure that the overall transmembrane pressure difference before and after cleaning shows a slightly increasing trend. 4.

As shown in Figure 2 b, when the total content of E6M and E6PM was 15 wt%, the contrast showed a trend of first increasing and then decreasing with increasing EP6M content E6PM.

As the content of monofunctional monomers continued to increase, although there was more adhesion on the glass interface, the network became very sparse, so the overall peel strength decreased, and the driving voltages of the film showed a decreasing trend.

The overall trend of T700 in the figure is similar to that of T300, showing an increasing trend.

Figure 15 illustrates a significant trend: the curvature of cracks escalates as the temperature (or stress level) rises during the phase of specimen damage.

With the increase of Capcure 3–800 content, the scattered-state and open-state transmittance of the samples both show an increasing trend.

An interesting outcome of the above averaging scheme is that a notable trend across the indented layers can now be perceived (blue filled square), especially for LSR.

LSR exhibits a decreasing trend along the build direction (V line), with a total difference of 5 GPa between the bottom and the top, which corresponds to a 0.8 GPa/mm gradient.

The overall transparency estimate demonstrated an average effect size of 0.288 (95% CI: −0.028–0.604), indicating a positive trend toward improved transparency across the materials analyzed.

According to the data presented in Figure 8 , when NZ-Ag + was used as a filter material, a decreasing trend of 222 Rn activity in the system was also obtained.

Due to the importance of adequate reporting quality for understanding and replicating research, an increasing trend in citation rate with higher reporting quality was expected.

The relative amplitude of the defect echo shows an increasing trend from 1 MHz to 2.25 MHz, and the relative amplitude of the defect echo corresponding to the 2.25 MHz frequency is the largest.

In the linear viscoelastic region (LVR) at small strains (<0.1), G′ remains relatively stable, with a clear trend of increasing stiffness as the glass bead concentration increases.

Additionally, we identified positive and highly significant correlations between Ni content and Cu, Mn, and Co; between Cu content and Mn and Co; and between Mn content and Co.

A P-value less than 0.05 is considered significant, less than 0.01 is highly significant, and less than 0.001 is extremely significant.

Across all three rotation speeds, the I D /I G ratio exhibits a decreasing trend with prolonged growth time, though a sudden increase occurs at 15 min.

As shown in Figure 4 , no significant differences in I D /I G were observed among CNTs prepared with varying Ni contents, while the CNT yield exhibited an increasing trend with higher Ni catalyst loading. 3.3.

The plastic viscosity of the fresh mortar was 0.726 Pa·s, which demonstrated a decreasing trend.

However, with increased disulfide bond density, the shape fixation rate of the materials showed a decreasing trend.

Overall, the disruptive effect of Al atoms on As-As bonds is highly significant.

After tempering at 200–800 °C, the hardness of the 1Cr13 specimens showed a trend of first increasing, then significantly decreasing and finally rapidly increasing with the increase in the tempering temperature, while the hardness of 2Cr13 showed a consistent decreasing trend, after tempering at 200–770 °C, with the increase in the tempering temperature.

Among these, the thermal decomposition temperatures of PBPR-1, PBPR-2, and PBPR-5 show a gradual increase, while the weight loss rate during decomposition exhibits an increasing trend.

Unsurprisingly, the dog-bone flakes processed with AO after extrusion, molding, and shredding show an increasing trend for OIt.

The moisture content of the solidified clay exhibited a decreasing trend as the number of freeze–thaw cycles increased.

Based on Figure 9 and Table 2 , it was revealed that the compressive strength and flexural strength of the new fast-curing polymer material sand consolidation exhibited an increasing trend with an increase in mesh number under the conditions of 10–15 mesh, 60–80 mesh, and 325 mesh.